OUR HIGH TENACITY POLYESTER TWISTED YARN IS MADE FROM 30-300TPM. STRENGTH CAN REACH TO 8.0CN/DTEX. IT IS WIDELY TO USE BELTS, FIRE HOSES, TEXTILE, CANVAS, V-BELTS, COATING CANVAS ETC.
Denier | Breaking strength | Breaking strength | Elongation at break | Do hot shrinkage rate | |||
D | dtex | N | Kg | cN/dtex | g/d | % | % |
500/96 | 555/96 | ≥45 | 4.6 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
1000/192 | 1110/192 | ≥90 | 9.2 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
1500/192 | 1670/192 | ≥135 | 13.8 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
2000/384 | 2220/384 | ≥180 | 18.4 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
3000/384 | 3330/384 | ≥270 | 27.6 | ≥8.1 | >9.0 | 13.5±2.0 | 6.5±0.5 |
Test Conditions | 177°C/10min |
OUR HIGH TENACITY POLYESTER TWISTED YARN IS MADE FROM 30-300TPM. STRENGTH CAN REACH TO 8.0CN/DTEX. IT IS WIDELY TO USE BELTS, FIRE HOSES, TEXTILE, CANVAS, V-BELTS, COATING CANVAS ETC.
Denier | Breaking strength | Breaking strength | Elongation at break | Do hot shrinkage rate | |||
D | dtex | N | Kg | cN/dtex | g/d | % | % |
500/96 | 555/96 | ≥45 | 4.6 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
1000/192 | 1110/192 | ≥90 | 9.2 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
1500/192 | 1670/192 | ≥135 | 13.8 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
2000/384 | 2220/384 | ≥180 | 18.4 | ≥8.1 | ≥9.0 | 13.5±2.0 | 6.5±0.5 |
3000/384 | 3330/384 | ≥270 | 27.6 | ≥8.1 | >9.0 | 13.5±2.0 | 6.5±0.5 |
Test Conditions | 177°C/10min |
HAITIAN NET & TWINE MANUFACTURERS
HUALING INDUSTRIAL FIELD, HANTING TOWN, CHENGXIANG DISTRICT,PUTIAN, FUJIAN, CHINA, 3511000
0086-13959558826
+0086-594-2083260
WWWCYZ@163.COM
Skype: WALLIARD1
QQ: 290559868